Investigation on the Efficient Removal of Particulate Matter (PM) with Biomass-Based Aerogel

Biomass-based aerogel is a new promising environmentally friendly filter material to remove fine particle matter and minimize air pollution. This study aims to investigate the air filtration properties of biomass-based aerogels via tests in a transparent chamber and verification in a real room with a burning smudge stick as a the particle source. The biomass-based aerogel used in this study is made of polysaccharides, protein and waste agricultural by-product (wheat straw). The addition of wheat straw contributes to the increase of surface area and complexity of the biomass-based aerogel pore structure. Compared with other commonly used commercial filtration materials including high-efficiency particulate air (HEPA) filter, surgical mask, regular cloth and silica aerogel, biomass-based aerogel K0.9G1.8S3.6WS1.8 shows excellent performance to remove PM 2.5 (99.50%) and PM 10 (99.40%) from the environment. When using the biomass-based aerogel, the filter core sample has a smaller volume and simpler structure than HEPA to achieve the similar filtration performance. The filtration performance of the biomass-based aerogels has been verified with a real room test. The current work demonstrates the high potential of biomass-based aerogels for infiltration application in different fields and provides an avenue to reuse agricultural by-products.


Introduction
Recently, air pollution is one of the main environmental problems in the world and is among the critical challenges facing modern societies. It refers to the contamination of the atmosphere by a mix of hazardous substances, particulate matter (PM) from natural sources and human activities. Natural forms of pollution are those that result from naturally occurring phenomena, such as volcanic eruptions, forest fire, ocean waves, soil dust. But the greatest contributor to pollution is human activities including industrial waste exhaust gas, fossil-fuel emissions, motor vehicle emissions, etc. Inhalable PM particles can be roughly divided into two size fractions PM 2.5 (aerodynamic diameter below 2.5 μm) and PM 10 (aerodynamic diameter between 2.5 μm and 10 μm) (Meng, Zhang, Yang, Yang, & Zhou 2016;Zoran, Savastru, Savastru, & Tautan 2020), both of those are fine inhalable particles and cannot be detected by naked eyes so that they are easily inhaled into human lung contributing to serious health problems . Between them, particles with a diameter less than 2.5 μm, which is only 3% of the diameter of a human hair, are also known as PM 2.5. They are easier to penetrate deep into the human lungs and some may even enter the bloodstream and circulatory system, causing cough and asthma, or even morbidity and mortality.
To solve this serious problem, researchers from all over the world are dedicated to studying various techniques to reduce air pollution. In the early period, the filter materials were mainly made of cotton, wool, jute, various synthetic fabrics of cellulose and other porous fabrics. Mandal and Srimani (1987) have used jute fiber as the filter in the microbiological experiment. In the 1940s, the highefficiency particulate air (HEPA) filter was invented in the USA (Zare Shahneh 2020) and then it was introduced into commercial applications in the following decade, such as air purification in special rooms. Since then, filter materials have developed rapidly and grown in popularity and necessity. In recent years, there are many novel air filter materials appeared in succession. Filtration materials are widely used in many applications including the typical heating ventilation and air conditioning (HVAC) systems, HEPA is also popular in the manufacture of face masks and personal protective equipment (PPE) during the COVID-19 pandemic. Hui Liu et al. (2020) created a kind of nanoscale polyacrylonitrile fiber filter using an innovative electronetting technique. It has been verified that the PM 0.3 was reduced by 99.996% with the novel nanonet filter. Abdul Rajak et al. (2020) used expanded polystyrene (EPS) waste as the raw material to make a nanofibrous membranes filter through the electrospinning method. Such nanofibrous membranes with low density and high Young's modulus can achieve high-efficiency PM 2.5 removal of 99.99% and a high-quality factor of 0.15 Pa -1 . Chao Jia et al. (2020) developed a kind of Al 2 O 3 -stabilized ZrO 2 submicron fiber air filter paper, which has high filtration efficiency (99.56%) and a low-pressure drop (108 Pa). At the same time, this material also shows excellent flexibility and thermal stability. Using the electrostatic induction-assisted solution blowing method, Shengnan Lv et al. (2018) fabricated PLA/PMMA composite nanofibers with 99.5% PM 2.5 removal. In the research of Wallace Woon FongLeung and Qiangqiang Sun, the improved nanofiber filter with charged fibers has been invented for capturing 100 nm aerosols, which are similar to that of the COVID-19 (Leung & Sun 2020).
Moreover, to date, most of the current filtration materials are 2D materials rather than 3D materials and the disposal process after usage has been rarely considered as some of them are harmful to the environment . Recently, various 3D-structured aerogels are widely used as adsorption materials due to their porous structure, 3D network structure and large surface area Wang, Chen, et al. 2019;Wang et al. 2018). The types of existing aerogel filtration materials are complex, such as graphene aerogel filter (Zhao et al. 2020), MoS 2 carbonized cellulose aerogel (Xie et al. 2021), polyimide nanofiber assembled aerogel (Qiao et al. 2021), etc. Furthermore, due to the limitation in the preparation of the aerogel filters, many of them are toxic and difficult to degrade in nature. To solve this, it has been applied the use of some nature-derived materials as the raw materials to produce aerogels, including cellulose (Li & Fu 2021), chitosan (Yin, Sun, Bao, & Li 2020), pectin (Groult, Buwalda, & Budtova 2021), alginate (Zhuang et al. 2020), starch (Ubeyitogullari & Ciftci 2016), gum arabic (L. Wang, Sánchez-Soto, & Abt 2016) whey protein (Buggy, McManus, Brodkorb, Hogan, & Fenelon 2018), egg white protein (Selmer, Kleemann, Kulozik, Heinrich, & Smirnova 2015), etc. Based on previous research, there are two main preparation methods used to manufacture biomass-based aerogels, the supercritical drying method and the freeze-drying method. Nowadays, it is a tendency that more and more studies are preferring to use the freeze-drying method because of its low cost and high safety. Freeze drying is a low-temperature dehydration process that the gelled sol is frozen and then dried through the sublimation process under a high vacuum. Konjac glucomannan (KGM) is a neutral heteropolysaccharide, its main chain composed of d-glucose (G) and d-mannoses (M) in a molar ratio of 1:1.6 linked by β-(1,4)-glycosidic bond (Behera & Ray 2016). Starch ) is a polymeric carbohydrate consisting of glucose, which can be classified into two kinds depending on the structure, i.e., amylose and amylopectin. Known as a kind of high molecular weight polypeptide, gelatin is widely used in many fields. Gelatin is derived from the partial hydrolysis of collagen, which is extracted from the animal byproduct (Guilherme et al. 2021) and it has a distinctive structure (Ge, Wu, Woshnak, & Mitmesser 2021). Wheat straw is an agricultural waste with low-cost renewable feedstocks that has the potential to be used in aerogel manufacture. Based on current serious situation of the COVID-19 pandemic, more attention has been placed on the air quality issues. Therefore, an attempt was made to find what is the best way to improve air quality by removing particles and apply filtration materials in different fields, such as HVAC systems in buildings, face masks, etc. Some current filter materials are not bio-degradable and may harm the environment. However, with the use of biomass materials, such as biomass-based aerogels, particles can be filtered and removed in an environmentally friendly way. By testing the particle number before and after the flow passing through the materials in an airtight negative pressure environment, Wu et al. (2021) studied the filtration performance of biomass-based aerogels of single layer and combined multilayers and the results show that the higher solid concentration of single layer biomass-based aerogel and the combination of aerogel pieces with different pore size distribution contribute to better filtration efficiency. Although the above research revealed the filtration performance of biomass-based aerogel in standard tests, the testing method and results have a limitation that the longtime filtration performance is not able to be reflected. This long-time performance is significantly meaningful when the filtration materials are used in practical applications. This study aims to test the air filtration properties of new biomass-based aerogels in a long period, an environmentally friendly and efficient filter, compared with other common commercial filtration materials including HEPA, surgical mask, regular cloth and silica aerogel. A purifier fitted with different types of filters, a testing chamber and a real room have been developed to simulate the air polluted environment and to test the PM removal ability of different materials.

Materials
KGM was provided by Licheng Biological Technology Co., Ltd. (Wuhan, China). Potato starch powder was obtained by Wuhan Lin He Ji Food Co., Ltd (Wuhan, China). Gelatin was purchased from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China).

Sol-gel solution preparation
The biomass-based aerogel was produced from KGM, gelatin, starch and wheat straw using the freeze drying method . This preparation method is based on three patents (Jiang 2013;Jiang 2020a;Jiang 2020b) and the previous research ). The gelatin particles were dissolved in water with water bathing at 60°C for 0.5 h. After dissolved totally, the water bath temperature was increased to 95°C, and then potato starch, wheat straw and KGM were gradually added and mixed with stirring speed of 600 rpm for one hour. In this research, there are three different solid concentrations selected and presented in Table 1. K, S, G and WS represent konjac glucomannan, potato starch, gelatin, wheat straw, respectively; the number after K, S, G and WS indicates the weight volume percent of composition in the original sol. Subsequently, the sol was injected into a cylindrical cell culture (15 cm) precooling and aging at 4°C.

Biomass-based aerogel preparation
After the aging process, the gel was frozen using an ultralow temperature freezer (LGT 2325, Liebherr Ltd) at -25°C for 10 h. Once completely frozen, the samples were placed in a freeze dryer (FD-1A-50, Biocool Ltd) drying at -55°C under a vacuum of one Pa for approximately 24 h to obtain biomass-based aerogel samples.

Microstructure observation with digital microscope
For the internal structure observation, the lab-scale KERN OBL 135C825 digital compound microscope with the adapted camera (ODC 825) has been used to observe the materials and take photos. All samples were cut into a small strip with the size of 4 cm * 2 cm. The eyepiece lens magnification is 10×/∅20 mm. The observation of different materials is carried out at the objective magnifications of 4× and 10×.

Microscope
Scanning Electron Microscopes (SEM) can be used to visualise the internal structure of different filters before and after PM capture. The tests were carried out at magnifications of ×50, ×200 and ×500 with an SEM (JEOL LV6060, Tokyo, Japan). The filter samples were coated with gold particles using a Gold and Platinum Sputter Coater.

PM generation and filtration measurements
To quantify the efficiency of PM filtration, a burning smudge stick was used as the source of PM particles. With a continuous supply, different sizes of particles will be produced for the test. The filtration efficiency of PM is measured using the apparatus shown in Figure 1. All the tests were implemented in a transparent chamber. On one side, an access door was set for changing samples. To provide a steady smog source, a small fan was placed on the left of the chamber and next to the burning smudge stick. Samples were cut as a disc with a diameter of 73 mm and used as the core of air purifier (B-D01, Acekool Portable Air Purifier). All samples were inserted into the plastic ring groove as shown in Figure 2. After passing through purifier, most of the PM 2.5 and PM 10 particles were intercepted by the filter materials, and the remain- where C1 represents the PM mass concentration before the start of air purifier and C2 represents the PM mass concentration after the start of air purifier.

Real room filtration tests
To further evaluate the PM filtration efficiency in practical applications, real room filtration tests have been carried out in a small room as shown in Figure 3. During the filtration test, the door and window in this room were closed to maintain the same test condition. After each test, the window and door will be opened to ventilate for the next test. Two smudge sticks, an air purifier (2415112EU, Leitz TruSens Z-1000 Air Purifier) with different filtration materials were placed on the table at the room corner.
For this real room test, the burning smudge sticks were used as the pollutant, and a PM detector was used for particulate matter concentration detection. In this test, the entire process was recorded, which could be divided into three stages: 1) the beginning stage of smudge stick burning; 2) the stage when PM particles in the room reached the maximum; 3) the final stage after turning on the air purifier. Because of the similar properties to PMs, burning smudge sticks were used to produce a large amount of smoke, which is representative of PM particles in this test. The Air purifier was placed next to the smudge stick to purify air in the room. A PM detector was used to evaluate the gaseous pollutant removal performance of different filtration materials. The removal efficiency of filters in the real room was also calculated based on Eq. 1. zCompared with the small transparent chamber filtration test, this real room experiment could represent practical air environment changes indoors.

Microstructure characterization of different filters
The internal morphology of biomass-based aerogel is a three-dimensional porous structure as shown in Figure 4.
With the addition of wheat straw, biomass-based aerogels showed a greenish-brown appearance before the test. It could be observed that wheat straw is randomly arranged in the pores of biomass-based aerogels. In addition, SEM was used for the observation of the internal structure details to ensure that wheat straw is evenly distributed inside the matrix thereby maximizing the surface area and the potential for PM filtration. From Figure 5, it could be found that the pore sizes of biomassbased aerogels with three different solid concentrations are different. The pore size of biomass-based aerogels began to have a significant increase with the increase of total solid concentration. The multi-cavities structure of wheat straw could be clearly observed, which contributes  to the increase of tiny holes in biomass-based aerogels and makes the biomass-based aerogel pore structure more complicated. After filtration test, color of the biomass-based aerogel has been changed significantly, and it was stained redbrown by smoke. Due to the small size of particles, they cannot be fully observed. But as illustrated in Figure 6, the intercepted large PM particles can be observed by microscope. In Figures 6 and 7, the particle sizes were measured using Image-Pro Plus 6.0 and the diameters of particles range from 7.1 to 62.8 μm.
The same test has also been carried out with the meltblown fabrics and non-woven fabrics and both are thin layers with a two-dimensional structure. As shown in Figure 7, the structure of the melt-blown cloth is dense, and few holes can be observed. However, there are too many open spaces in the fibres of non-woven fabric, which can allow particles to pass through. PM particles could be observed in these two fabrics, but the particles on nonwoven fabrics are relatively less than melt-blown fabrics and biomass-based aerogels. The SEM images of different filters are presented in Figure 8. As demonstrated, the pore size of non-woven fabric and silica aerogel is larger than that of melt-blown fabric, regular cloth and biomassbased aerogel K0.9G1.8S3.6WS1.8. The multi-cavities structure of wheat straw also could be found in the biomass-based aerogels.

PM filtration performance test in the transparent chamber
As introduced in section 2.4.3, the PM filtration performance was measured by using a handmade transparent chamber with a small fan, smudge stick, air purifier and PM detector. In this study, the PM 2.5 and PM 10 filtration efficiency of different filters was calculated by comparing the particle concentration before and after the start of air purifier. Every test lasted one hour, during the first 30 minutes the smudge stick was burned completely. In the next 30 minutes, the particle concentrations were measured and the data was recorded every minute. With the work of different filters, PM particles have been removed at different rates. As shown in Figure 9, the filters have good filtration performance compared with regular cloth and silica aerogel. In the beginning, there are full of particles in the transparent chamber and the filtration efficiencies of all samples are zero in the first five minutes. At the fifth minute, the curve for HEPA starts to increase dramatically, converges gradually and finally reaches the highest filtration efficiency of 98.80% at the thirtieth minute. Compared with the HEPA filter, a one-minute delay can be observed for three types of biomass-based aerogels to start to remove particles. Biomass-based aerogel K0.9G1.8S3.6WS1.8 shows a similar growth rate with HEPA at the beginning, but its growth rate begins to exceed HEPA at around 15 minutes. At last, the removal efficiency of K0.9G1.8S3.6WS1.8 reaches 99.50% at the thirtieth minute, which is the highest among all filters. On the other hand, the filtration performance of K0.5G1S2WS1 is worse than the other two biomass-based aerogels (89.79%) because it has low solid concentration, which results in the low density and a large number of open pores in the structure of biomass-based aerogels. The particle removal efficient rates of three biomass-based aerogels are different. With a high density and relatively dense structure, the K0.9G1.8S3.6WS1.8 has the highest  growth rate followed by the K0.7G1.4S2.8WS1.4. In the beginning, there is a difference in their growth rate and this difference between them becomes more obvious as the experiment continued. At the end of the test, PM 2.5 removal efficiency of K0.7G1.4S2.8WS1.4. is 89.79%. At the ninth minute, the surgical mask starts to work and has a similar growth rate of HEPA and K0.9G1.8S3.6WS1.8. At the end of the test, the removal efficiency of surgical mask reached 97.90%, which means good PM 2.5 filtration performance. To be more specific, Figure 9(b) was used to magnify the details and compare PM 2.5 removal efficiency of HEPA, surgical mask and biomassbased aerogel K0.9G1.8S3.6WS1 from 26 minutes to 30 minutes. It could be found that the filtration efficiency of HEPA decreases at the 30th minute, while the filtration efficiency of biomass-based aerogel K0.9G1.8S3.6WS1.8 continuously increases and eventually higher than that of HEPA at the end. In this test, the two worst removal efficiencies were observed with silica aerogel (83.78%) and regular cloth (58.56%). To confirm the effect of particle sizes, the filtration tests of PM 10 were also studied, and the results are shown in Figure 10. Compared with the removal test of PM 2.5, the removal efficiency curve of PM 10 has a similar tendency, in which the filtration performance of HEPA and biomass-based aerogel K0.9G1.8S3.6WS1 (99.40%) are better than other filters with a relatively high growth rate. If removal efficiency of 97% is taken as the standard, the K0.9G1.8S3.6WS1, HEPA  can meet the requirement. The removal efficiencies reach as high as above 99% for both PM 2.5 and PM 10 for biomass-based aerogel with the formula K0.9G1.8S3.6WS1. The high promised removal efficiencies for PM 2.5 and PM 10 are attributed to the composite pore structure, the high specific surface area formed by the specific structure of wheat straw and the freeze-drying method.
In the freeze-drying process, the pores were formed by the ice crystals sublimation and the pore wall was composed of solid materials. The porous structure of biomassbased aerogel provides a good foundation for filtration performance. With the addition of wheat straw, the internal structure becomes more complicated due to the special multi-cavities structure of wheat straw (as shown in Figure 5). When particles entered the biomass-based aerogels, most of them will be intercepted inside the biomass-based aerogels because of the complicated 3D structure leading to higher filtration performance. Besides, for K0.7G1.4S2.8WS1.4, K0.5G1S2WS1, silica aerogel and regular cloth, there is a little difference in the filtration efficiency between PM 2.5 and PM 10. The efficiency of removing PM 2.5 with regular cloth (58.56%) is higher than the efficiency of using it to remove PM 10 (25.33%), and this difference was significant as shown in Figure 9(a) and Figure 10(a).

Monitoring of indoor ambient air quality with different filters
The detailed PM 2.5, PM 10 concentrations were recorded, removal efficiencies were calculated following the procedure as above, and the results are shown in Figures 11 and 12. As demonstrated by the purple curve in Figure 11( Figure 12 shows the PM 10 concentration and removal efficiency during the whole testing process. The HEPA is usually made of chemical fibers or glass fibers, with a diameter of about 0.5 μm to 2 μm, which is smaller than PM 10 particles. In general, the interception dominates to achieve the filtration efficiency when the particles have a larger size than the fiber diameter. It can be found in Figure 12(a) that PM 10 concentration in the real room was decreased rapidly when started to use HEPA as the filter. Meanwhile, the filtration rate of the biomass-based aerogel K0.9G1.8S3.6WS1.8 and K0.7G1.4S2.8WS1.4 is slower than HEPA. This could be explained that the biomass-based aerogel is a thin disc with a thickness of about 3 mm, which is much thinner than that of HEPA. Besides, the pleated HEPA structure contributes to the maximum efficiency function. When using the biomass-based aerogel, the filter core sample has a smaller volume and a simple structure.

Conclusion
Biomass-based aerogels were successfully fabricated by the freeze-drying method with relatively low energy consumption. The complex 3D porous structure of biomass-based aerogels provides the condition and leads to good filtration performance. The addition of wheat straw improves surface area of biomass-based aerogel and affects the aerogel pore structure due to its special multi-cavity structure. The filtration performance comparison between biomass-based aerogels and some current commercial filters indicates the great potential of biomass-based aerogels as filtration materials for removing PM 2.5 and PM 10 in different fields. PM 2.5 and PM 10 removal efficiencies of biomass-based aerogel K0.9G1.8S3.6WS1 in a small transparent chamber have been determined to be 99.50% and 99.40%, respectively. HEPA shows a similar effect having removal efficiencies of 98.80 for PM 2.5 and 98.20% for PM 10. However, in terms of size, the HEPA filter is much thicker than biomass-based aerogels, and its maximum efficiency func-